عنوان اصلی: بازيابي واناديم از سرباره فولادسازي كنورتور LD به روش هيدرومتالورژي
پدیدآورندگان : رشته مهندسي متالورژي ومواد-دانشكده مهندسي متالورژي و مواد (پديدآور)
نوع : متن
جنس : پايان نامه
صاحب محتوا :

کتابخانه دیجیتالی دانشگاه تهران

وضعیت نشر :
مشخصات فیزیکی : جلدnull - ص پنج,93
خلاصه : In order to extract vanadium from LD (Linz-Donawitz) converter slag of steelmaking plant an alkaline roasting-acid leaching study was carried out and effect of different parameters on the kinetics of vanadium dissolution was determined. The leaching residue was characterized by XRD, XRF and SEM/EDX analyzer. The maximum vanadium recovery of ca. 95% was achieved at the optimum leaching condition of 70 ?C, S/L: 1/15, acid concentration: 3M, agitation rate: 600 rpm, particle size: blew 850 µm and leaching time: 150 minutes. Dissolution of vanadium in sulfuric acid showed that there are two stages in the kinetics of leaching. In the first 15 minutes, a sharp increase in the amount of vanadium extracted was observed and at longer times, leaching became slower. Shrinking core model (SCM) was used to describe the kinetics of the slag acid leaching. SCM equations were modified to represent the long time leaching process in which the initial recovery of vanadium (at the beginning of long term period) is not zero. It was found that the kinetics of leaching at low temperature is controlled by chemical reaction for both short and long leaching periods. Rate of leaching is controlled by solid product diffusion regime at high temperature.Due to high iron concentration in the aquous solution an iron precipitation stage was necessary before the solvent extraction process. Iron removal was carried out using Na2S as precipitating agent. 90% 0f iron was precipitated using sodium sulphide at S2-/Fe3+ ratio of 10 at 65 ?C. After this treatment, iron powder was added to obtain an electric potential about 200-250 mV in order to reduce iron from Fe3+ to Fe2+ which is not extractable by D2EHPA. Under the optimum condition of room temperature, O/A: 1, D2EHPA concentration: 20%, diluent: Kerosene, mixing time: 10 min and pH 2-2.5, 94% of vanadium was extracted by this organic solution.
یادداشت :
چكيده: به فارسي و انگليسي
كتابنامه: به فارسي و انگليسي
به همراه cd
عنوان به انگليسي:Recovery of Vanadium from LD Converter Slags Using Hydrometallurgical Process
گرايش استخراج فلزات
كارشناسي ارشد
شناسه : oai:ut.ac.ir:thesis/1-212691
تاریخ ایجاد رکورد : 1389/2/29
تاریخ تغییر رکورد : 1389/3/24
قیمت شيء دیجیتال : دارای قیمت

راهنمای سفارش دیجیتال سازی

* محتوای این صفحه توسط کارشناسان این درگاه ویرایش نشده است. لطفا در صورت مشاهده ایراد در محتوا از این طریق اطلاع رسانی کنید.

دیدگاه شما

تست
ورود به درگاه کنسرسیوم
Loding



رمز عبور خود را فراموش کرده ام.
چنانچه تا کنون عضو سایت نشده اید ثبت نام کنید.
درباره کنسرسیوم
ما مجموعه‌ای از كتابخانه‌ها و سازمان‌های دارای منابع اطلاعاتی (کتاب، نشریه، نسخه‌های خطی، عکس، صدا، فیلم و... ) هستیم که با هدف تامین نیازهای پژوهشگران و شهروندان ایرانی برای دسترسی هر چه سریع‌تر به محتوای مورد نظر خود، کنسرسیوم محتوای ملی را تشکیل داده‌ایم. برای رسیدن به این هدف، قصد داریم با بسترسازی مناسب و جلب مشارکت دیگر تولید کنندگان محتوا به گرد آوری، تبدیل، سازماندهی و حفاظت اطلاعات به شکل رقومی و در سطح ملی، بپردازیم.