عنوان اصلی: حذف فلز سنگين سرب از پساب صنعتي با استفاده از نانوذرات مغناطيسي آهن
پدیدآورندگان : گروه مهندسي عمران-محيط زيست-دانشكده محيط زيست (پديدآور)
نوع : متن
جنس : پايان نامه
صاحب محتوا :

کتابخانه دیجیتالی دانشگاه تهران

وضعیت نشر :
مشخصات فیزیکی : جلدnull - ص سيزده,96
خلاصه : At this work the adsorption of Pb in battery industry wastewater onto magnetite nanopatticles has been studied. The magnetite nanoparticles synthesis by coprecipitation of Fe(II) and Fe(III) ions in precense of ammonia . the average size distribution of particles was determined by particle analyzer instrument . The average diameter was determined to be 26.5 nm, in TEM images, nanoparticles were spherical. The adsorption of Pb+2 on magnetite nanoparticles was investigated in different condition of solution pH, magnetite content, initial concentration, tempreature, shaker rpm. By increasing solution pH from 2 to 12 the adsorption percentage reached from 15 to 100. The much higher of adsorption took plase in first ten minuts and by increasment of magnetite concentration from 2 to 5 gl-1 reached from 50 to 98 percent.Initial concentration effect was investigated on adsorption process and equilibrium data fitted by Lungmuir and Fruindlich isotherms. The Lungmuir isotherm has better fitness with equilibrium data and by this isotherm the maximum loading capacity of magnetite nanoparticles was determined. The adsorption of Pb+2 ions increased as temperature from 10oC to 70oC. lead adsorption rate increased nearly 55 to 99 percent . The shaker revolution was studied on adsorption and showed that increasing the amount of 100-400 prcent of mixer adsorption of lead from 81% to nearly 99%. In higher rpm, the shaker rpm had no influence on adsorption efficiency and the adsorption was unchanged in rpm above 150rpm. The separation of lead bounded magnetite was done through magnetic separator which designed in laboratory. The magnetite nanoparticles retained by using two magnetic field less than 1 TESLA. Recovery of magnetic was done by using acid. By this method 75% of lead desorbed which indicates that lead adsorption by magnetite nanoparticles is reversible. In order to increase longevity, maintain magnetism, improved chemical stability, better dispersion in the reaction environment and to prevent iron oxide nanoparticles being changed into magnetite nanoparticles Magmayt are coating by silica. This work done by sol-gel method polymer Si(Et)4 in a mixture of ethanol ammonia is done. FT-IR results of Fe3O4-SiO2 nanoparticles that expression of adsorption peak of the curve in this phase magnetite Fe-O vibration and vibration for Si-O Fe3O4-SiO2 confirms.Key words: Removal of lead, Magnetite iron Nanoparticles, Battery industry wastewater
یادداشت :
به همراه cd
چكيده: به فارسي و انگليسي
كتابنامه: به فارسي و انگليسي
عنوان به انگليسي:Removal heavy metal of lead(Pb) from industrial wastewater by magnetite iron nanoparticles
عمران - محيط زيست
كارشناسي ارشد
شناسه : oai:ut.ac.ir:thesis/1-212664
تاریخ ایجاد رکورد : 1389/2/29
تاریخ تغییر رکورد : 1389/3/24
قیمت شيء دیجیتال : دارای قیمت

راهنمای سفارش دیجیتال سازی

* محتوای این صفحه توسط کارشناسان این درگاه ویرایش نشده است. لطفا در صورت مشاهده ایراد در محتوا از این طریق اطلاع رسانی کنید.

دیدگاه شما

تست
ورود به درگاه کنسرسیوم
Loding



رمز عبور خود را فراموش کرده ام.
چنانچه تا کنون عضو سایت نشده اید ثبت نام کنید.
درباره کنسرسیوم
ما مجموعه‌ای از كتابخانه‌ها و سازمان‌های دارای منابع اطلاعاتی (کتاب، نشریه، نسخه‌های خطی، عکس، صدا، فیلم و... ) هستیم که با هدف تامین نیازهای پژوهشگران و شهروندان ایرانی برای دسترسی هر چه سریع‌تر به محتوای مورد نظر خود، کنسرسیوم محتوای ملی را تشکیل داده‌ایم. برای رسیدن به این هدف، قصد داریم با بسترسازی مناسب و جلب مشارکت دیگر تولید کنندگان محتوا به گرد آوری، تبدیل، سازماندهی و حفاظت اطلاعات به شکل رقومی و در سطح ملی، بپردازیم.