عنوان اصلی: بهينه‌سازي پارامترهاي عملياتي فرآيند مگ مولكولي با استفاده از نانوذرات مغناطيسي جهت جداسازي يون سلنيوم
پدیدآورندگان : ياسر (پديدآور)
نبوي لاريمي (پديدآور)
سيدمحمدعلي (پديدآور)
موسويان (پديدآور)
جابر (مشاور)
صفدري (مشاور)
محمد حسن (پديدآور)
ملاح (پديدآور)
گروه مهندسي شيمي-دانشكده فني (پديدآور)
نوع : متن
جنس : پايان نامه
صاحب محتوا :

کتابخانه دیجیتالی دانشگاه تهران

وضعیت نشر :
خلاصه : In the present Original research, the absorption of selenium ions by magnetite and Amine-functionalized-magnetite nanoparticles, have been studied. Experiments have been performed both in batch and continuous (Fixed bed column) processes. In batch part, the effect of pH, type of acid (to bring the pH to the desired pH), temperature, contact time and initial concentration of selenium ions, and in the continuous part, three important design parameters, ie flow rate, column height and column diameter were tested. In the first step pH in the range of 1 to 9.4 was tested. The optimum pH for magnetite 2.4 and Amine-functionalized-magnetite 1.7 are obtained. Then, three types of acid, HCl, HNO3 and H2SO4 were used at optimal pH and acid H2SO4 was considered the best. Absorption at temperatures higher than 30oC is endothermic and exothermic at lower temperatures than 30oC. In order to obtain the kinetic parameters, the pseudo-first-order, pseudo-second-order, intraparticle diffusion and Elovich kinetic models were used to modeling of experimental data and pseudo-second-order model has showed the best fit among the models. Analysis of Elovich model showed that adsorption on magnetite is chemical while amine-functionalized-magnetite has physisorption mechanism. Two parameter Langmuir, Freundlich and Temkin isotherms, three parameter Sips, Redlich-Peterson and Toth isotherms and four parameter fritz-schlunder isotherm were used to model the equilibrium isotherms. Results showed that by increasing the number of parameters in a model it becomes more flexible and will show better fitting results to experimental data. In continuous modes, the results showed that the optimal flow rate for amine-functionalized-magnetite and magnetite are respectively 1 and 4 ml/min. In these set experiments, the diameter of the column was 1 cm and feed concentration for magnetite and amine-functionalized-magnetite 50 and 30 mg/L respectively. Adsorbent particles used in the column have size between 200 and 300 microns. Height increase causes a little increasing in selenium uptake, but will significantly increase absorption percent of selenium and changing column diameter, had no great impact on the absorption rate and performance of column. Models of Thomas, Yan and Yoon-Nelson were used to model breakthrough curves and Thomas model have better adaptation with experimental data.
یادداشت :
به همراه cd
چكيده: به فارسي و انگليسي
عنوان به انگليسي:Optimization of Operating Parameter of Magmolecule Process Using Magnetic Nanoparticles for Selenium Ion Separation
كتابنامه: به فارسي و انگليسي
رشته مهندسي شيمي-طراحي فرآيندها
كارشناسي ارشد
شناسه : oai:ut.ac.ir:thesis/1-255788
تاریخ ایجاد رکورد : 1391/12/6
تاریخ تغییر رکورد : 1392/2/16
قیمت شيء دیجیتال : دارای قیمت

راهنمای سفارش دیجیتال سازی

* محتوای این صفحه توسط کارشناسان این درگاه ویرایش نشده است. لطفا در صورت مشاهده ایراد در محتوا از این طریق اطلاع رسانی کنید.

دیدگاه شما

تست
ورود به درگاه کنسرسیوم
Loding



رمز عبور خود را فراموش کرده ام.
چنانچه تا کنون عضو سایت نشده اید ثبت نام کنید.
درباره کنسرسیوم
ما مجموعه‌ای از كتابخانه‌ها و سازمان‌های دارای منابع اطلاعاتی (کتاب، نشریه، نسخه‌های خطی، عکس، صدا، فیلم و... ) هستیم که با هدف تامین نیازهای پژوهشگران و شهروندان ایرانی برای دسترسی هر چه سریع‌تر به محتوای مورد نظر خود، کنسرسیوم محتوای ملی را تشکیل داده‌ایم. برای رسیدن به این هدف، قصد داریم با بسترسازی مناسب و جلب مشارکت دیگر تولید کنندگان محتوا به گرد آوری، تبدیل، سازماندهی و حفاظت اطلاعات به شکل رقومی و در سطح ملی، بپردازیم.